HOTSHORT Meaning and
Definition
-
Hotshort refers to a term primarily used in the context of metallurgy and materials science, describing a specific type of brittleness or failure that occurs with certain alloys or metals. When a material is hotshort, it becomes susceptible to cracking, fracturing, or otherwise failing at high temperatures or during hot working processes.
The hotshort phenomenon is typically observed in alloys or materials that contain a high concentration of certain impurities, such as sulfur or phosphorus, or when they have a low melting point. These impurities segregate along grain boundaries or other defects within the material, weakening its structure. Consequently, when the material is exposed to high temperatures, the impurities cause localized embrittlement, significantly decreasing its resistance to deformation or stress.
The term "hotshort" is often seen in association with the behavior of steel, especially when it contains high sulfur content. When hotshortness occurs, the material becomes more prone to failure when subjected to hot forging, rolling, or extrusion processes. It is crucial for manufacturers and engineers to take hotshortness into consideration during the design and selection of materials, as it can affect the overall integrity and quality of the final product.
To mitigate the effects of hotshortness, various techniques can be employed, such as refining the material's composition, carefully controlling the temperature and processing conditions, or employing alloying elements to counteract the detrimental effects of impurities.
Common Misspellings for HOTSHORT
- gotshort
- botshort
- notshort
- jotshort
- uotshort
- yotshort
- hitshort
- hktshort
- hltshort
- hptshort
- h0tshort
- h9tshort
- horshort
- hofshort
- hogshort
- hoyshort
- ho6short
- ho5short
- hotahort
- hotzhort
Etymology of HOTSHORT
The term "Hotshort" originated from the welding and metallurgy industry. Its etymology can be understood by breaking down the word into its two components: "hot" and "short".
The word "hot" refers to the high temperature at which the process takes place. In metallurgy, high temperatures are often required for shaping or forming metal. The term "hot" suggests the need for elevated temperatures to carry out the process.
The term "short" in this context is used to describe the brittleness or susceptibility of certain types of metals when subjected to high temperatures. When a metal becomes "short" in this sense, it means it has lost its strength, toughness, or ductility, becoming brittle and easily breakable. This can occur due to the presence of impurities or certain alloying elements in the metal.